 Product Name:
|
|
PVC tackifier
|
|
Use:
|
|
This product is applied to enhance the PVC paste resin and polyester cloth, nylon cloth, cotton cloth adhesive strength, mainly used in manufacturing PVC belt, PVC tarpaulin, PVC advertising cloth and other products, is simple, use less, high adhesion strengths.
|
|
Package:
|
|
Use of iron sealed package, specifications: 200 kg / drum
|
|
Store
|
This product should be hermetically stored at 5-40 ℃, ventilated, cool, dry place; low-temperature conditions, give rise to higher viscosity of the product easy to mix artificial, should try to avoid this product with alcohol, water and other products contact.
|
|
Usage:
|
Spray: to spray on the cloth PVC accelerator surface, then the PVC paste resin coated cloth, and then go to 100 ℃ drying Road about pre-plasticized, and then into the 150-180 ℃ full of baked Road The plasticization.
PVC promoter mixed with the PVC paste resin. PVC paste resin at 3-8% of the PVC to add accelerator to stir evenly. In the mixing process to prevent overheating caused by increased viscosity of PVC paste resin. Mixed good PVC paste resin as primer, uniform mixing apply on the surface of cloth and went to 100 ℃ or so pre-bake Road plasticization. Again in the pre-plasticizing the PVC surface, roll coated with a layer of PVC did not increase promoter of PVC paste resin, into the baking Road 130-160 ℃ full plasticization. (Note: PVC paste resin should be a good mix that with the use, preferably within half an hour to 1 hour one-time run out.)
Adhesive properties: peel strength of PVC, polyester fabric> = 190N, 5cm, PVC / nylon fabric> = 200N/5cm, PVC / nylon fabric> = 200N/5cm
|
|
Safty Notice:
|
This product is on the eyes, skin, respiratory tract stimulation, operation should bring rubber gloves and glasses to prevent contact with skin and eyes. Plasticization bake Road or Breath devices must meet the exhaust device, to prevent inhalation of the respiratory tract in the oligomer.
|
|