 Product Name:
|
|
Adhesives
|
|
Use:
|
Adhesive Bonding agent 2001 is a one-component adhesive without solvent, was used to improve the sol coating for PVC plasticized polyester, polyamide, or aramid fiber substrate adhesion.
|
|
Package:
|
Use of iron sealed package, specifications: 220 kg / drum
|
|
Store
|
|
This product should be hermetically stored at 5-40 ℃, ventilated, cool, dry place; low-temperature conditions, give rise to higher viscosity of the product easy to mix artificial, should try to avoid this product with alcohol, water and other products contact.
|
|
Usage:
|
Adhesives 2001 mixed with the PVC paste resin. In the PVC paste resin binder added to 3-8% in 2001 to carry out mixing evenly. In the mixing process to prevent overheating caused by increased viscosity of PVC paste resin. Mixed good PVC paste resin as primer, uniform mixing apply on the surface of cloth and went to 100 ℃ or so pre-bake Road plasticization. Again in the pre-plasticizing the PVC surface, roll coated with a layer of PVC did not increase promoter of PVC paste resin, into the baking Road 130-160 ℃ full plasticization. (Note: PVC paste resin should be a good mix that with the use, preferably within half an hour to 1 hour one-time run out.)
Adhesive properties: peel strength of PVC, polyester fabric> = 190N, 5cm, PVC / nylon fabric> = 200N/5cm, PVC / nylon fabric> = 200N/5cm.
|
|
Safty Notice:
|
This product is on the eyes, skin, respiratory tract stimulation, operation should bring rubber gloves and glasses to prevent contact with skin and eyes. Plasticization bake Road or Breath devices must meet the exhaust device, to prevent inhalation of the respiratory tract in the oligomer.
|
|